Product
Brand
|
MgO
% Min.
|
Grading
mm
|
Setting
|
Sintering
Temp. C
|
Cr2O3
Min.
|
|
CC-MG-MORT
|
85
|
0-0.5
|
Cermaics
|
1600
|
-
|
|
CC-MG-MORT(W)
|
90
|
0-0.5
|
Cermaics
|
1620
|
-
|
|
CC-MCN-MORT
|
60
|
0-1.0
|
Cermaics
|
1650
|
15
|
|
CC-CMN-MORT
|
40
|
0-1.0
|
Cermaics
|
1650
|
25
|
|
CC-LM-(C)
X
|
70
|
0-2.0
|
Cermaics
|
800
|
8
|
|
Product
Brand
|
Al2O3
% Min.
|
Grading
|
Setting
|
Sintering
Temp. C
|
|
CC-30
|
30
|
0-0.5
|
Cermaics
|
1400
|
|
CC-40
|
40
|
0-0.5
|
Cermaics
|
1350
|
|
CC-42
|
42
|
0-0.5
|
Cermaics
|
1370
|
|
CC-50
|
50
|
0-0.5
|
Cermaics
|
1350
|
|
CC-50
|
52-54
|
0-0.5
|
Cermaics
|
1350
|
|
CC-70A
|
65-70
|
0-0.5
|
Cermaics
|
1350
|
|
CC-75B
|
70-75
|
0-0.5
|
Cermaics
|
1400
|
Alumina Motars
Insulation Motars
Castables
|
Product
Brand
|
Al2O3
% Min.
|
Grading
in mm
|
Max
services Temp. in C
|
B.D.
gms/cc Min.
|
C.S.S
kgs/cm2 Min.
|
Thermal
Conductivity KAC/m/hr 500 C
|
|
INSC-1100
|
32-35
|
0.6
|
1100
|
0.9-1.0
|
13-16
|
0.28
|
|
INSC-1250
|
35-38
|
0.6
|
1250
|
1.25-1.35
|
35+5
|
0.33
|
|
INSC-1300
|
40
|
0.6
|
1300
|
1.5-1.6
|
30-40
|
0.44
|
|
INSC-1350
|
35
|
0.6
|
1350
|
1.6+0.05
|
60-80
|
0.40+0.02
|
|
INSC-1350S
|
35
|
0.6
|
1350
|
1.5+0.5
|
40-50
|
0.32+0.02
|
|
Product
Brand
|
Max.
Service Temp. C
|
Grading
in mm
|
Setting
|
Al2O3
% Min.
|
Fe2O3
% Max.
|
B.D.
gms/cc Min.
|
C.S.S
kgs/cm 24 hes
|
P.C.E
O.C Min.
|
Sintering
Temp.C
|
|
CAST-45
|
1400
|
0-4
|
Hydraulic
|
45
|
2
|
2.2
|
300
|
31-32
|
1250
|
|
CAST-50
|
1450
|
0-4
|
Hydraulic
|
52-53
|
2
|
2.25
|
200
|
34
S.K
|
1250
|
|
CAST-60
|
1500
|
0-4
|
Hydraulic
|
60
|
2
|
2-2.25
|
200
|
35
S.K
|
1400
|
|
CAST-60
|
1550
|
0-4
|
Hydraulic
|
62+2
|
1.5
|
2.3
|
250
|
34
|
1350
|
|
CAST-70
|
1550
|
0-4
|
Hydraulic
|
70
|
5.5
|
2.4
|
250
|
35
|
1200
|
|
CAST-80
|
1600
|
0-4
|
Hydraulic
|
80
|
4-5
|
2.5-2.8
|
250
|
35
|
1400
|